Hittebestande staal gietstuk EN10295
Ons onderneming produseer hittebestande staal in ooreenstemming met Europese standaarde, bied aanpassing van verwerking, welkom om te koop
Meganiese eienskappe bykamertemperatuur
|
Aanwysing |
Hitte behandeling |
Trek proefneming |
Hardheid Hb maksimum. |
||||||
|
Simbool |
Temperatuur grade |
FPO, 2 MPA a min. |
Rm MPA a min. |
A % min. |
|||||
|
Naam |
Nommer |
||||||||
|
Ferrities en austenities - Ferritiese grade |
Gx30crsiz b |
1.4710 |
+AC |
800 tot 850 |
300 |
||||
|
GX40CRSI13 |
1.4729 |
+AC |
800 tot 850 |
300 |
|||||
|
GX40CRSI17 |
1.4740 |
+AC |
800 tot 850 |
300 |
|||||
|
GX40CRSI24 |
1.4745 |
Nee hitte behandeling |
d |
||||||
|
GX40CRSI28 |
1.4776 |
d |
|||||||
|
GX130CRSI29 |
1.4777 |
d |
|||||||
|
GX160CRSI18 |
1.4743 |
d |
|||||||
|
Gx40crnisi 27-4 |
1.4823 |
250 |
550 |
3 |
d |
||||
|
Austenitiese grade |
Gx25crnisi 18-9 |
1.4825 |
230 |
450 |
15 |
||||
|
Gx40crnisi 22-10 |
1.4826 |
230 |
450 |
8 |
|||||
|
Gx25crnisi 20-14 |
1.4832 |
230 |
450 |
10 |
|||||
|
Gx40crnisi 25-12 |
1.4837 |
220 |
450 |
6 |
|||||
|
Gx40crnisi 25-20 |
1.4848 |
220 |
450 |
8 |
|||||
|
Gx40crnisinb 24-24 |
1.4855 |
220 |
450 |
4 |
|||||
|
Gx35nicrsi 25-21 |
1.4805 |
220 |
430 |
8 |
|||||
|
Gx40nicrsi 35-17 |
1.4806 |
220 |
420 |
6 |
|||||
|
Gx40nicrsinb 35-18 |
1.4807 |
220 |
420 |
4 |
|||||
|
Gx40nicrsi 38-19 |
1.4865 |
220 |
420 |
6 |
|||||
|
Gx40nicrsinb 38-19 |
1.4849 |
220 |
420 |
4 |
|||||
|
Gx10nicrsinb 32-20 |
1.4859 |
180 |
440 |
20 |
|||||
|
Gx40nicrsi 35-26 |
1.4857 |
220 |
440 |
6 |
|||||
|
Gx40nicrsinb 35-26 |
1.4852 |
220 |
440 |
4 |
|||||
|
Gx50nicrco 20-20-20 |
1.4874 |
320 |
420 |
6 |
|||||
|
Gx50nicrcow 35-25- 15-5 |
1.4869 |
270 |
480 |
5 |
|||||
|
Gx40nicrnb 45-35 |
1.4889 |
240 |
440 |
3 |
|||||
|
Nikkel en kobalt |
basislegerings |
G-NICR28W |
2.4879 |
240 |
440 |
3 |
|||
|
G -cocr28 |
2.4778 |
235 |
490 |
6 |
|||||
|
G-NICR50NB |
2.4680 |
230 |
540 |
8 |
|||||
|
G-NICR15 |
2.4815 |
200 |
400 |
3 |
|||||
|
A 1MPA =1 n/mm2 b As hierdie graad gebruik word vir slytasies, kan dit gelewer word sonder hittebehandeling . C +'n middel: uitgloeiing d gietstukke kan ook in die uitgegloeide toestand voorsien word, in welke geval 'n maksimum hardheidswaarde ooreengekom kan word . |
|||||||||